- 熔体流动速率 [g/10min]: 43.0
- 密度 [g/cm3]: 0.956
- 弯曲强度 [MPa]: 3.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.956 g/cc | 0.0345 lb/in³ | Exxon Method |
| Apparent Bulk Density | 0.577 g/cc | 0.0208 lb/in³ | ASTM D1895 (B) |
| Viscosity | 1400 cP @Temperature 121 °C | 1400 cP @Temperature 250 °F | melt viscosity; ASTM D-3236 |
| Melt Flow | 43 g/10 min | 43 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 3.00 MPa | 435 psi | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 61.0 °C | 142 °F | Exxon Method |
| Vicat Softening Point | 105 °C | 221 °F | Softening Point, R&B; ASTM E-28 |