- 熔体流动速率 [g/10min]: 1.4
- 密度 [g/cm3]: 0.9265
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.9265 g/cc | 0.03347 lb/in³ | ASTM D1505 | ||
| Vinyl Acetate Content | 4.0 % | 4.0 % | |||
| Thickness | 31.8 microns | 1.25 mil | |||
| Melt Flow | 1.4 g/10 min | 1.4 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882 | ||
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 | ||
| Dart Drop | 9.84 g/micron | 250 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 27.6 MPa | 4000 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 21.4 MPa | 3100 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 145 MPa | 21000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 179 MPa | 26000 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 4.4 % | 4.4 % | ASTM D1003 | ||
| Gloss | 72 % | 72 % | at 45º; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 182 - 199 °C | 360 - 390 °F | with BUR of 1.5:1 or higher | ||
| Blow-up Ratio (BUR) | 2.5 | 2.5 | |||
| Descriptive Properties | |||||
| process | Film | ||||
| region | US & Canada | ||||