- 熔体流动速率 [g/10min]: 0.8
- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.374
- 弯曲强度 [MPa]: 52.4
- 弯曲模量 [MPa]: 2.28
- 热变形温度 [℃]: 88.9
- 透光率 [%]: 84.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | weight gain after 24 hr. immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0080 cm/cm | 0.0030 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 0.80 g/10 min @Load 3.80 kg, Temperature 230 °C | 0.80 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 50 | 50 | ASTM D785 |
| Tensile Strength, Ultimate | 52.4 MPa | 7600 psi | ASTM D638 |
| Tensile Modulus | 2.28 GPa | 330 ksi | ASTM D638 |
| Flexural Strength | <= 86.2 MPa | <= 12500 psi | ASTM D790 |
| Flexural Modulus | 2.28 GPa | 330 ksi | ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm | 0.700 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.202 W/m-K | 1.40 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 88.9 °C | 192 °F | annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.4 °C | 175 °F | annealed; ASTM D648 |
| Vicat Softening Point | 85.0 °C | 185 °F | 50°C/hr; 50N; ASTM D1525 |
| 96.1 °C | 205 °F | 50°C/hr; 10N; ASTM D1525 | |
| Optical Properties | Metric | English | Comments |
| Haze | 98 % @Thickness 3.17 mm | 98 % @Thickness 0.125 in | Diffusion; ASTM D1003 |
| Transmission, Visible | 84 % @Thickness 3.17 mm | 84 % @Thickness 0.125 in | ASTM D1003 |