- 熔体流动速率 [g/10min]: 4.5
- 密度 [g/cm3]: 1.16
- 缺口冲击强度: 0.53
- 弯曲强度 [MPa]: 50.0
- 透光率 [%]: 91.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| Melt Flow | 4.5 g/10 min | 4.5 g/10 min | Condition 230/3.8; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
| Elongation at Break | 5.3 % | 5.3 % | ASTM D638 |
| Modulus of Elasticity | 2.00 GPa | 290 ksi | ASTM D638 |
| Flexural Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Gardner Impact | 3.30 J | 2.43 ft-lb | ASTM D3029 GB |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.0 °C | 174 °F | ASTM D648 |
| Vicat Softening Point | 112 °C | 234 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 91.3 % | 91.3 % | Luminous Transmittance, ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 221 - 254 °C | 430 - 489 °F | |