- 熔体流动速率 [g/10min]: 1.428
- 密度 [g/cm3]: 1.19
- 透光率 [%]: 91.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Melt Flow | 1.428 g/10 min @Load 3.80 kg, Temperature 230 °C | 1.428 g/10 min @Load 8.38 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.5 % | 3.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 3.60 GPa | 522 ksi | 1 mm/min; ISO 527 |
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C | 223 °F | ISO 75 |
| Vicat Softening Point | 119 °C | 246 °F | B/50; ISO 306 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.51 | 1.51 | ISO 489 |
| Transmission, Visible | 91 % | 91 % | D65/10°; ISO 13468-2 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 - 250 °C | 428 - 482 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | <= 109 °C | <= 228 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |