- 熔体流动速率 [g/10min]: 9.5
- 弯曲模量 [MPa]: 1.86
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ISO 1183 |
| Water Absorption | <= 0.30 % | <= 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ISO 294 |
| Melt Flow | 9.5 g/10 min @Load 3.80 kg, Temperature 230 °C | 9.5 g/10 min @Load 8.38 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 36.5 MPa | 5300 psi | ISO 527 |
| Elongation at Break | 44 % | 44 % | ISO 527 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO 527 |
| Tensile Modulus | 1.93 GPa | 280 ksi | ISO 527 |
| Flexural Strength | 57.2 MPa | 8300 psi | ISO 178 |
| Flexural Modulus | 1.86 GPa | 270 ksi | ISO 178 |
| Izod Impact, Unnotched (ISO) | 3.40 kJ/m² @Diameter 4.00 mm | 1.62 ft-lb/in² @Diameter 0.157 in | bar; ISO 180 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 108 µm/m-°C @Temperature 0.000 - 100 °C | 60.0 µin/in-°F @Temperature 32.0 - 212 °F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 216 °F | annealed; ISO 75 |
| Vicat Softening Point | 110 °C | 230 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 0.0 % | 0.0 % | Opaque; ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 221 - 249 °C | 430 - 480 °F | Cylinder Temp |
| Melt Temperature | 221 - 249 °C | 430 - 480 °F | |
| Mold Temperature | 48.9 - 85.0 °C | 120 - 185 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |