- 熔体流动速率 [g/10min]: 2.0
- 吸水率 [%]: 0.11
- 缺口冲击强度: 0.16
- 拉伸强度 [MPa]: 57.23
- 弯曲模量 [MPa]: 3.13
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Water Absorption | 0.11 % | 0.11 % | 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 2.0 g/10 min @Load 5.00 kg, Temperature 200 °C | 2.0 g/10 min @Load 11.0 lb, Temperature 392 °F | Procedure A Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 75 | 75 | ASTM D785 |
| Tensile Strength, Yield | 57.23 MPa | 8301 psi | 2 in per min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 3.13 GPa | 454 ksi | ASTM D638 |
| Izod Impact, Notched | 0.160 J/cm | 0.300 ft-lb/in | 0.125 inch bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C | 169 °F | ASTM D648 |
| Vicat Softening Point | 97.7 °C | 208 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90 % | 90 % | ASTM D1003 |