- 熔体流动速率 [g/10min]: 1.495
- 密度 [g/cm3]: 1.15
- 拉伸强度 [MPa]: 46.0
- 热变形温度 [℃]: 99.0
- 透光率 [%]: 81.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 | ||
| Melt Flow | 1.495 g/10 min @Load 3.80 kg, Temperature 230 °C | 1.495 g/10 min @Load 8.38 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | 50 mm/min; ISO 527 | ||
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527 | ||
| Tensile Modulus | 1.90 GPa | 276 ksi | 1 mm/min; ISO 527 | ||
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature 23.0 °C | 23.8 ft-lb/in² @Temperature 73.4 °F | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 90.0 µm/m-°C @Temperature 0.000 - 50.0 °C | 50.0 µin/in-°F @Temperature 32.0 - 122 °F | ASTM E831 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | ISO 75 | ||
| Vicat Softening Point | 91.0 °C | 196 °F | B50; ISO 306 | ||
| Glass Transition Temp, Tg | 107 °C | 225 °F | IEC 10006 | ||
| Glow Wire Test | 700 °C | 1290 °F | IEC 695-2 | ||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 81 % | 81 % | Transmission Factor; DIN 5036 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 230 - 260 °C | 446 - 500 °F | Barrel Temperature | ||
| Die Temperature | 260 °C | 500 °F | |||
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | |||
| Drying Temperature | <= 85.0 °C | <= 185 °F | Predrying | ||
| Dry Time | 2 - 3 hour | 2 - 3 hour | Desiccant-type drier | ||
| Descriptive Properties | |||||
| Energy Half Angle | 20° | IEC 695-2 | |||
| Fire Rating | B2 | DIN 4102 | |||