- 密度 [g/cm3]: 1.33
- 缺口冲击强度: 1.87
- 断裂伸长率 [%]: 62.0
- 弯曲强度 [MPa]: 41.0
- 硬度: 101.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 - 1.37 g/cc | 0.0480 - 0.0495 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 101 | 101 | ASTM D785 |
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
| Elongation at Break | 130 % | 130 % | |
| Modulus of Elasticity | 2.372 GPa | 344.0 ksi | |
| Flexural Yield Strength | 62.0 MPa | 8990 psi | ASTM D790 |
| Izod Impact, Notched | 1.87 J/cm @Temperature 23.0 °C | 3.50 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | annealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | V-0, 5V; UL Standard 94 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 163 - 200 °C | 325 - 392 °F | Forming Temperature |