- 密度 [g/cm3]: 1.34
- 缺口冲击强度: 9.6
- 断裂伸长率 [%]: 64.0
- 弯曲强度 [MPa]: 47.0
- 弯曲模量 [MPa]: 2.41
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 47.0 MPa | 6820 psi | ASTM D638 |
| Modulus of Elasticity | 2.183 GPa | 316.6 ksi | ASTM D638 |
| Flexural Yield Strength | 64.0 MPa | 9280 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 9.60 J/cm @Thickness 3.17 mm | 18.0 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 160 - 171 °C | 320 - 340 °F | |
| Adapter Temperature | 171 - 177 °C | 340 - 350 °F | |
| Die Temperature | 171 - 177 °C | 340 - 350 °F | |
| Melt Temperature | <= 204 °C | <= 399 °F | |
| Dry Time | 0.0 hour | 0.0 hour | Drying typically not required |