- 密度 [g/cm3]: 1.18
- 弯曲强度 [MPa]: 62.0
- 弯曲模量 [MPa]: 2.96
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 98.5 | 98.5 | ISO 2039-2 |
| Tensile Strength, Ultimate | 62.0 MPa | 8990 psi | 5 mm/min; ISO 527 |
| Flexural Strength | 105 MPa | 15200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.96 GPa | 429 ksi | 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | 2.17 J/cm² | 10.3 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.120 J/cm² | 0.571 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | >= 110 °C | >= 230 °F | ISO 306A |
| Flammability, UL94 | HB | HB | |
| Flammability Test | 3.0 | 3.0 | BS 476, Pt7 |