- 密度 [g/cm3]: 1.16
- 缺口冲击强度: 7.0
- 弯曲强度 [MPa]: 50.0
- 弯曲模量 [MPa]: 2.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 45 | 45 | ISO 2039-2 |
| Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 25 % | 25 % | 5 mm/min; ISO 527 |
| Flexural Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | >= 105 °C | >= 221 °F | ISO 306A |
| Flammability, UL94 | HB | HB | |