- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 1.18
- 吸水率 [%]: 0.3
- 缺口冲击强度: 2.2
- 弯曲模量 [MPa]: 3.40
- 热变形温度 [℃]: 106.0
- 透光率 [%]: 92.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
| Melt Flow | 0.80 g/10 min | 0.80 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 99 | 99 | ISO 2039-2 |
| Ball Indentation Hardness | 190 MPa | 27600 psi | ISO 2039-1 (H 961-30) |
| Tensile Strength | 85.0 MPa | 12300 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 |
| Flexural Modulus | 3.40 GPa | 493 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 2.20 kJ/m² | 1.05 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 2.60 J/cm² | 12.4 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.220 J/cm² | 1.05 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 71.0 µm/m-°C | 39.4 µin/in-°F | ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ISO 75B |
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 216 °F | ISO 75A |
| Vicat Softening Point | 108 °C | 226 °F | ISO 306B |
| 115 °C | 239 °F | ISO 306A | |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | IEC 695-2-1 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ISO 489 |
| Haze | 0.40 % | 0.40 % | ASTM D1003 |
| Transmission, Visible | 92 % | 92 % | ASTM D1003 |