- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 1.15
- 吸水率 [%]: 0.37
- 缺口冲击强度: 8.0
- 弯曲模量 [MPa]: 1.50
- 透光率 [%]: 89.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Water Absorption | 0.37 % | 0.37 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | |
| Melt Flow | 0.90 g/10 min | 0.90 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 25 | 25 | ISO 2039-2 |
| Tensile Strength | 43.0 MPa | 6240 psi | ISO 527 |
| Elongation at Break | 40 % | 40 % | ISO 527 |
| Flexural Strength | 50.0 MPa | 7250 psi | ISO 178 |
| Flexural Modulus | 1.50 GPa | 218 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.850 J/cm² | 4.04 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 120 µm/m-°C | 66.7 µin/in-°F | ASTM E831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | ISO 75A |
| Vicat Softening Point | 92.0 °C | 198 °F | ISO 306B |
| 107 °C | 225 °F | ISO 306A | |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | IEC 695-2-1 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ISO 489 |
| Haze | 3.0 % | 3.0 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |