- 熔体流动速率 [g/10min]: 6.3
- 密度 [g/cm3]: 1.17
- 缺口冲击强度: 0.32
- 透光率 [%]: 91.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D-792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D-955 |
| Melt Flow | 6.3 g/10 min @Load 3.80 kg, Temperature 230 °C | 6.3 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 58.4 MPa | 8470 psi | ASTM D-638 |
| Elongation at Break | 4.6 % | 4.6 % | ASTM D-638 |
| Modulus of Elasticity | 3.25 GPa | 472 ksi | ASTM D-638 |
| Flexural Strength | 86.25 MPa | 12510 psi | ASTM D-790 |
| Izod Impact, Notched | 0.320 J/cm @Thickness 6.35 mm | 0.600 ft-lb/in @Thickness 0.250 in | ASTM D-256 |
| Gardner Impact | 1.58 J @Thickness 3.17 mm | 1.17 ft-lb @Thickness 0.125 in | Falling Weight; ASTM D-3029 GB |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 70.0 µm/m-°C | 38.9 µin/in-°F | ASTM D-696 |
| Maximum Service Temperature, Air | 50.0 °C | 122 °F | UL-746 ABC |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.3 °C | 182 °F | ASTM D-648 |
| Vicat Softening Point | 112 °C | 233 °F | ASTM D-1525 |
| Flammability, UL94 | HB | HB | |
| Optical Properties | Metric | English | Comments |
| Haze | <= 1.5 % | <= 1.5 % | ASTM D-1003 |
| Transmission, Visible | 91.6 % | 91.6 % | ASTM D-1003 |