- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.123
- 吸水率 [%]: 0.02
- 缺口冲击强度: 0.2
- 拉伸强度 [MPa]: 13.8
- 断裂伸长率 [%]: 20.0
- 弯曲强度 [MPa]: 13.0
- 弯曲模量 [MPa]: 1.50
- 硬度: 42.0
- 热变形温度 [℃]: 94.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.123 - 1.56 g/cc | 0.00444 - 0.0564 lb/in³ | Average value: 1.23 g/cc Grade Count:176 |
| Filler Content | 30.0 - 40.0 % | 30.0 - 40.0 % | Average value: 39.7 % Grade Count:83 |
| Water Absorption | 0.0200 - 0.0400 % | 0.0200 - 0.0400 % | Average value: 0.0267 % Grade Count:15 |
| Linear Mold Shrinkage | 0.00300 - 0.0200 cm/cm | 0.00300 - 0.0200 in/in | Average value: 0.00948 cm/cm Grade Count:137 |
| Linear Mold Shrinkage, 6.35 mm section | 0.0100 - 0.0120 cm/cm | 0.0100 - 0.0120 in/in | Average value: 0.0116 cm/cm Grade Count:5 |
| Linear Mold Shrinkage, Transverse | 0.00560 - 0.0165 cm/cm | 0.00560 - 0.0165 in/in | Average value: 0.0126 cm/cm Grade Count:18 |
| Melt Flow | 1.00 - 30.0 g/10 min | 1.00 - 30.0 g/10 min | Average value: 10.1 g/10 min Grade Count:155 |
| Ash | 34.0 - 45.0 % | 34.0 - 45.0 % | Average value: 39.9 % Grade Count:19 |
| 37.0 - 63.0 % @Temperature 600 - 600 °C | 37.0 - 63.0 % @Temperature 1110 - 1110 °F | Average value: 42.0 % Grade Count:5 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 50.0 - 100 | 50.0 - 100 | Average value: 64.5 Grade Count:6 |
| Hardness, Rockwell R | 42.0 - 102 | 42.0 - 102 | Average value: 84.8 Grade Count:34 |
| Hardness, Shore D | 65.0 - 84.0 | 65.0 - 84.0 | Average value: 72.8 Grade Count:20 |
| Tensile Strength, Ultimate | 13.0 - 50.0 MPa | 1890 - 7250 psi | Average value: 27.5 MPa Grade Count:115 |
| 7.00 - 18.0 MPa @Temperature 60.0 - 120 °C | 1020 - 2610 psi @Temperature 140 - 248 °F | Average value: 12.3 MPa Grade Count:1 | |
| Tensile Strength, Yield | 13.8 - 60.0 MPa | 2000 - 8700 psi | Average value: 29.2 MPa Grade Count:75 |
| Elongation at Break | 3.00 - 70.0 % | 3.00 - 70.0 % | Average value: 10.1 % Grade Count:77 |
| Elongation at Yield | 2.00 - 25.0 % | 2.00 - 25.0 % | Average value: 5.21 % Grade Count:72 |
| Modulus of Elasticity | 1.40 - 5.17 GPa | 203 - 750 ksi | Average value: 3.21 GPa Grade Count:45 |
| Flexural Yield Strength | 20.0 - 75.0 MPa | 2900 - 10900 psi | Average value: 48.4 MPa Grade Count:98 |
| Flexural Modulus | 1.50 - 5.70 GPa | 218 - 827 ksi | Average value: 3.22 GPa Grade Count:173 |
| 0.450 - 1.40 GPa @Temperature 60.0 - 120 °C | 65.3 - 203 ksi @Temperature 140 - 248 °F | Average value: 0.883 GPa Grade Count:1 | |
| Compressive Yield Strength | 51.7 MPa | 7500 psi | Average value: 51.7 MPa Grade Count:3 |
| Izod Impact, Notched | 0.200 - 1.33 J/cm | 0.375 - 2.50 ft-lb/in | Average value: 0.378 J/cm Grade Count:102 |
| 0.200 - 0.300 J/cm @Temperature -40.0 - -20.0 °C | 0.375 - 0.562 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.267 J/cm Grade Count:2 | |
| Izod Impact, Unnotched | 0.300 - 9.08 J/cm | 0.562 - 17.0 ft-lb/in | Average value: 2.82 J/cm Grade Count:34 |
| 0.200 - 0.200 J/cm @Temperature 0.000 - 0.000 °C | 0.375 - 0.375 ft-lb/in @Temperature 32.0 - 32.0 °F | Average value: 0.200 J/cm Grade Count:2 | |
| Izod Impact, Notched (ISO) | 2.00 - 12.0 kJ/m² | 0.952 - 5.71 ft-lb/in² | Average value: 4.05 kJ/m² Grade Count:14 |
| 1.60 - 3.00 kJ/m² @Temperature -40.0 - -20.0 °C | 0.761 - 1.43 ft-lb/in² @Temperature -40.0 - -4.00 °F | Average value: 2.18 kJ/m² Grade Count:9 | |
| Charpy Impact Unnotched | 1.70 - 1000 J/cm² | 8.09 - 4760 ft-lb/in² | Average value: 4.44 J/cm² Grade Count:23 |
| 0.900 - 6.40 J/cm² @Temperature -40.0 - -20.0 °C | 4.28 - 30.5 ft-lb/in² @Temperature -40.0 - -4.00 °F | Average value: 1.77 J/cm² Grade Count:22 | |
| Charpy Impact, Notched | 0.200 - 2.70 J/cm² | 0.952 - 12.8 ft-lb/in² | Average value: 0.477 J/cm² Grade Count:59 |
| 0.100 - 0.600 J/cm² @Temperature -40.0 - -20.0 °C | 0.476 - 2.86 ft-lb/in² @Temperature -40.0 - -4.00 °F | Average value: 0.193 J/cm² Grade Count:46 | |
| Gardner Impact | 0.565 - 13.6 J | 0.417 - 10.0 ft-lb | Average value: 2.05 J Grade Count:32 |
| 1.35582 - 1.35582 J @Temperature -30.0 - -5.56 °C | 1.00000 - 1.00000 ft-lb @Temperature -22.0 - 22.0 °F | Average value: 3.11 J Grade Count:2 | |
| 4.86 - 4.86 J @Temperature -23.0 - -23.0 °C | 3.58 - 3.58 ft-lb @Temperature -9.40 - -9.40 °F | Average value: 3.11 J Grade Count:1 | |
| 4.86 - 4.86 J @Thickness 3.18 - 3.18 mm | 3.58 - 3.58 ft-lb @Thickness 0.125 - 0.125 in | Average value: 3.11 J Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 - 1.00e+16 ohm-cm | 1.00e+15 - 1.00e+16 ohm-cm | Average value: 8.50e+15 ohm-cm Grade Count:6 |
| Dielectric Constant | 2.60 - 4.80 | 2.60 - 4.80 | Average value: 3.15 Grade Count:4 |
| Dielectric Strength | 19.7 - 24.0 kV/mm | 500 - 610 kV/in | Average value: 21.4 kV/mm Grade Count:7 |
| Dissipation Factor | 0.00800 | 0.00800 | Average value: 0.00800 Grade Count:3 |
| Arc Resistance | 120 sec | 120 sec | Average value: 120 sec Grade Count:3 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:7 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 41.4 - 172 µm/m-°C | 23.0 - 95.6 µin/in-°F | Average value: 67.7 µm/m-°C Grade Count:11 |
| Thermal Conductivity | 0.317 W/m-K | 2.20 BTU-in/hr-ft²-°F | Average value: 0.317 W/m-K Grade Count:3 |
| Melting Point | 150 - 182 °C | 302 - 360 °F | Average value: 159 °C Grade Count:19 |
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 - 150 °C | 201 - 302 °F | Average value: 127 °C Grade Count:137 |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 - 142 °C | 133 - 287 °F | Average value: 81.1 °C Grade Count:144 |
| Vicat Softening Point | 54.0 - 165 °C | 129 - 329 °F | Average value: 118 °C Grade Count:73 |
| Flammability, UL94 | HB | HB | Grade Count:79 |
| Flammability Test | 0.800 - 125 | 0.800 - 125 | Average value: 75.4 Grade Count:5 |
| Oxygen Index | 21.0 - 22.0 % | 21.0 - 22.0 % | Average value: 21.1 % Grade Count:8 |
| Glow Wire Test | 650 - 750 °C | 1200 - 1380 °F | Average value: 738 °C Grade Count:49 |
| Optical Properties | Metric | English | Comments |
| Gloss | 20.0 - 40.0 % | 20.0 - 40.0 % | Average value: 32.3 % Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 193 - 227 °C | 380 - 440 °F | Average value: 210 °C Grade Count:5 |
| Nozzle Temperature | 200 - 238 °C | 392 - 460 °F | Average value: 226 °C Grade Count:27 |
| Melt Temperature | 170 - 279 °C | 338 - 534 °F | Average value: 224 °C Grade Count:93 |
| Mold Temperature | 18.0 - 80.0 °C | 64.4 - 176 °F | Average value: 51.2 °C Grade Count:96 |
| Drying Temperature | 65.6 - 104 °C | 150 - 219 °F | Average value: 76.7 °C Grade Count:76 |
| Dry Time | 1.00 - 6.00 hour | 1.00 - 6.00 hour | Average value: 2.71 hour Grade Count:73 |
| Moisture Content | 0.0100 - 0.200 % | 0.0100 - 0.200 % | Average value: 0.0685 % Grade Count:20 |
| Injection Pressure | 2.76 - 120 MPa | 400 - 17400 psi | Average value: 67.4 MPa Grade Count:73 |
| Hold Pressure | 2.07 - 51.7 MPa | 300 - 7500 psi | Average value: 7.47 MPa Grade Count:15 |
| Back Pressure | 0.345 - 2.00 MPa | 50.0 - 290 psi | Average value: 1.24 MPa Grade Count:51 |