- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.98
- 吸水率 [%]: 0.02
- 缺口冲击强度: 0.267
- 拉伸强度 [MPa]: 14.0
- 断裂伸长率 [%]: 16.0
- 弯曲强度 [MPa]: 12.0
- 弯曲模量 [MPa]: 0.800
- 硬度: 50.0
- 热变形温度 [℃]: 50.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.980 - 1.10 g/cc | 0.0354 - 0.0397 lb/in³ | Average value: 1.04 g/cc Grade Count:82 |
| Filler Content | 15.0 - 20.0 % | 15.0 - 20.0 % | Average value: 19.9 % Grade Count:35 |
| Water Absorption | 0.0200 - 0.0300 % | 0.0200 - 0.0300 % | Average value: 0.0211 % Grade Count:9 |
| Linear Mold Shrinkage | 0.00100 - 0.0190 cm/cm | 0.00100 - 0.0190 in/in | Average value: 0.0125 cm/cm Grade Count:60 |
| Linear Mold Shrinkage, 6.35 mm section | 0.0200 cm/cm | 0.0200 in/in | Average value: 0.0200 cm/cm Grade Count:7 |
| Melt Flow | 0.900 - 70.0 g/10 min | 0.900 - 70.0 g/10 min | Average value: 14.1 g/10 min Grade Count:59 |
| Ash | 18.0 - 23.0 % | 18.0 - 23.0 % | Average value: 20.0 % Grade Count:13 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 50.0 - 98.0 | 50.0 - 98.0 | Average value: 81.2 Grade Count:24 |
| Hardness, Shore D | 65.0 - 72.0 | 65.0 - 72.0 | Average value: 69.8 Grade Count:12 |
| Tensile Strength, Ultimate | 12.0 - 30.3 MPa | 1740 - 4400 psi | Average value: 22.5 MPa Grade Count:39 |
| Tensile Strength, Yield | 14.0 - 32.0 MPa | 2030 - 4640 psi | Average value: 25.1 MPa Grade Count:52 |
| Elongation at Break | 2.00 - 545 % | 2.00 - 545 % | Average value: 75.1 % Grade Count:59 |
| Elongation at Yield | 3.00 - 100 % | 3.00 - 100 % | Average value: 10.7 % Grade Count:23 |
| Modulus of Elasticity | 1.00 - 2.69 GPa | 145 - 390 ksi | Average value: 1.80 GPa Grade Count:22 |
| Flexural Yield Strength | 16.0 - 54.0 MPa | 2320 - 7830 psi | Average value: 36.5 MPa Grade Count:45 |
| Flexural Modulus | 0.800 - 2.70 GPa | 116 - 392 ksi | Average value: 1.65 GPa Grade Count:80 |
| Compressive Yield Strength | 27.6 - 47.6 MPa | 4000 - 6900 psi | Average value: 40.9 MPa Grade Count:3 |
| Izod Impact, Notched | 0.267 - 7.47 J/cm | 0.500 - 14.0 ft-lb/in | Average value: 1.07 J/cm Grade Count:73 |
| Izod Impact, Unnotched | 0.534 - 5340 J/cm | 1.00 - 10000 ft-lb/in | Average value: 9.81 J/cm Grade Count:19 |
| Izod Impact, Notched (ISO) | 3.80 - 16.0 kJ/m² | 1.81 - 7.61 ft-lb/in² | Average value: 7.07 kJ/m² Grade Count:7 |
| 3.30 - 3.30 kJ/m² @Temperature -40.0 - -40.0 °C | 1.57 - 1.57 ft-lb/in² @Temperature -40.0 - -40.0 °F | Average value: 3.30 kJ/m² Grade Count:1 | |
| Izod Impact, Unnotched (ISO) | 15.0 - 20.0 kJ/m² | 7.14 - 9.52 ft-lb/in² | Average value: 17.7 kJ/m² Grade Count:3 |
| Gardner Impact | 0.983 - 40.7 J | 0.725 - 30.0 ft-lb | Average value: 13.4 J Grade Count:29 |
| 2.71164 - 18.5295 J @Temperature -30.0 - -5.56 °C | 2.00000 - 13.6667 ft-lb @Temperature -22.0 - 22.0 °F | Average value: 14.7 J Grade Count:3 | |
| 20.8 - 20.8 J @Temperature -23.0 - -23.0 °C | 15.3 - 15.3 ft-lb @Temperature -9.40 - -9.40 °F | Average value: 14.7 J Grade Count:1 | |
| 20.8 - 20.8 J @Thickness 3.18 - 3.18 mm | 15.3 - 15.3 ft-lb @Thickness 0.125 - 0.125 in | Average value: 14.7 J Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | Average value: 1.00e+16 ohm-cm Grade Count:7 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 63.0 - 80.0 µm/m-°C | 35.0 - 44.4 µin/in-°F | Average value: 68.7 µm/m-°C Grade Count:3 |
| Melting Point | 160 - 182 °C | 320 - 360 °F | Average value: 168 °C Grade Count:4 |
| Deflection Temperature at 0.46 MPa (66 psi) | 50.0 - 118 °C | 122 - 245 °F | Average value: 95.9 °C Grade Count:63 |
| Deflection Temperature at 1.8 MPa (264 psi) | 40.6 - 106 °C | 105 - 223 °F | Average value: 59.7 °C Grade Count:56 |
| Vicat Softening Point | 70.0 - 150 °C | 158 - 302 °F | Average value: 112 °C Grade Count:9 |
| Flammability, UL94 | HB | HB | Grade Count:22 |
| Optical Properties | Metric | English | Comments |
| Gloss | 55.0 - 75.0 % | 55.0 - 75.0 % | Average value: 67.5 % Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 193 - 227 °C | 380 - 440 °F | Average value: 210 °C Grade Count:7 |
| Nozzle Temperature | 200 - 227 °C | 392 - 440 °F | Average value: 217 °C Grade Count:11 |
| Melt Temperature | 170 - 302 °C | 338 - 576 °F | Average value: 215 °C Grade Count:17 |
| Mold Temperature | 4.00 - 91.0 °C | 39.2 - 196 °F | Average value: 44.4 °C Grade Count:22 |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | Average value: 77.6 °C Grade Count:13 |
| Dry Time | 1.00 - 3.00 hour | 1.00 - 3.00 hour | Average value: 1.73 hour Grade Count:13 |
| Moisture Content | 0.0100 - 0.0500 % | 0.0100 - 0.0500 % | Average value: 0.0400 % Grade Count:8 |
| Injection Pressure | 2.76 - 103 MPa | 400 - 15000 psi | Average value: 54.3 MPa Grade Count:15 |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | Average value: 5.17 MPa Grade Count:6 |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi | Average value: 0.689 MPa Grade Count:6 |