- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.9
- 缺口冲击强度: 0.32
- 拉伸强度 [MPa]: 33.8
- 弯曲模量 [MPa]: 1.41
- 硬度: 99.0
- 热变形温度 [℃]: 101.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ASTM D-1505 | ||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C | 12 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D-1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 99 | 99 | ASTM D-785 | ||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D-638 | ||
| Elongation at Yield | 11 % | 11 % | 2 in/min (20 mm/min); ASTM D-638 | ||
| Flexural Modulus | 1.41 GPa | 205 ksi | ASTM D-790 | ||
| Izod Impact, Notched | 0.320 J/cm | 0.600 ft-lb/in | @23°; ASTM D-256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ASTM D-648 | ||
| Descriptive Properties | |||||
| process | Injection Molding | ||||