- 熔体流动速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.91
- 拉伸强度 [MPa]: 23.0
- 弯曲模量 [MPa]: 0.680
- 硬度: 62.0
- 热变形温度 [℃]: 62.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | MD; ASTM D955 |
| Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 62 | 62 | ASTM D785 |
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | ASTM D638 |
| Elongation at Break | 350 % | 350 % | ASTM D638 |
| Tensile Modulus | 0.680 GPa | 98.6 ksi | ASTM D638 |
| Flexural Strength | 30.0 MPa | 4350 psi | ASTM D790 |
| Flexural Modulus | 0.680 GPa | 98.6 ksi | ASTM D790 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 62.2 °C | 144 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 47.8 °C | 118 °F | |