- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.12
- 缺口冲击强度: 1.01
- 拉伸强度 [MPa]: 77.01
- 弯曲模量 [MPa]: 4.699
- 硬度: 105.0
- 热变形温度 [℃]: 155.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
| Ash | 27 - 33 % | 27 - 33 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength, Yield | 77.01 MPa | 11170 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 4.499 GPa | 652.5 ksi | ASTM D638 |
| Flexural Strength | 80.0 MPa | 11600 psi | ASTM D790 |
| Flexural Modulus | 4.699 GPa | 681.5 ksi | ASTM D790 |
| Izod Impact, Notched | 1.01 J/cm | 1.90 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | |