- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.21
- 缺口冲击强度: 0.694
- 拉伸强度 [MPa]: 81.98
- 弯曲模量 [MPa]: 7.2988
- 硬度: 105.0
- 热变形温度 [℃]: 145.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | MD; ASTM D955 |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
| Ash | 40 % | 40 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength at Break | 81.98 MPa | 11890 psi | ASTM D638 |
| Tensile Strength, Yield | 81.98 MPa | 11890 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 4.599 GPa | 667.1 ksi | ASTM D638 |
| Flexural Strength | 117.0 MPa | 16970 psi | ASTM D790 |
| Flexural Modulus | 7.2988 GPa | 1058.6 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm | 1.30 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | |