- 熔体流动速率 [g/10min]: 18.0
- 密度 [g/cm3]: 1.03
- 缺口冲击强度: 2.14
- 拉伸强度 [MPa]: 17.0
- 弯曲模量 [MPa]: 1.20
- 硬度: 55.0
- 热变形温度 [℃]: 86.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | MD; ASTM D955 |
| Melt Flow | 18 g/10 min | 18 g/10 min | ASTM D1238 |
| Ash | 20 % | 20 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 55 | 55 | ASTM D785 |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 1.500 GPa | 217.5 ksi | ASTM D638 |
| Flexural Strength | 20.0 MPa | 2900 psi | ASTM D790 |
| Flexural Modulus | 1.20 GPa | 174 ksi | ASTM D790 |
| Izod Impact, Notched | 2.14 J/cm | 4.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 86.1 °C | 187 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.8 °C | 127 °F | |