- 密度 [g/cm3]: 1.21
- 缺口冲击强度: 0.91
- 弯曲强度 [MPa]: 81.0
- 弯曲模量 [MPa]: 6.20
- 硬度: 107.0
- 热变形温度 [℃]: 170.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 107 | 107 | ASTM D785 |
| Tensile Strength, Ultimate | 81.0 MPa | 11700 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 139 MPa | 20200 psi | ASTM D790 |
| Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
| Izod Impact, Notched | 0.910 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.00 J/cm | 7.49 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 229 - 246 °C | 444 - 475 °F | Approximate middle barrel temperature range |