- 密度 [g/cm3]: 1.07
- 缺口冲击强度: 0.21
- 弯曲强度 [MPa]: 17.0
- 弯曲模量 [MPa]: 2.10
- 硬度: 98.0
- 热变形温度 [℃]: 118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 98 | 98 | ASTM D785 |
| Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
| Elongation at Break | 74.3 % | 74.3 % | ASTM D638 |
| Flexural Strength | 49.0 MPa | 7110 psi | ASTM D790 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ASTM D790 |
| Izod Impact, Notched | 0.210 J/cm | 0.393 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.60 J/cm | 10.5 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 210 - 221 °C | 410 - 430 °F | Approximate middle barrel temperature range |