- 熔体流动速率 [g/10min]: 15.0
- 缺口冲击强度: 0.57
- 拉伸强度 [MPa]: 54.0
- 弯曲模量 [MPa]: 4.13
- 热变形温度 [℃]: 160.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Melt Flow | 15 g/10 min | 15 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Modulus | 4.13 GPa | 599 ksi | ASTM D790 |
| Izod Impact, Notched | 0.570 J/cm | 1.07 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ASTM D648 |