- 熔体流动速率 [g/10min]: 2.5
- 缺口冲击强度: 2.13
- 拉伸强度 [MPa]: 65.0
- 弯曲模量 [MPa]: 4.203
- 硬度: 86.0
- 热变形温度 [℃]: 157.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Melt Flow | 2.5 g/10 min | 2.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 86 | 86 | ASTM D785 |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 83.0 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 4.203 GPa | 609.6 ksi | ASTM D790 |
| Izod Impact, Notched | 2.13 J/cm | 3.99 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.00 J/cm | 15.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 157 °C | 315 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | ASTM D648 |