- 熔体流动速率 [g/10min]: 20.0
- 缺口冲击强度: 0.75
- 拉伸强度 [MPa]: 24.0
- 弯曲模量 [MPa]: 1.135
- 硬度: 85.0
- 热变形温度 [℃]: 108.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.905 g/cc | 0.905 g/cc | ASTM D792 |
| Melt Flow | 20 - 30 g/10 min @Temperature 230 °C | 20 - 30 g/10 min @Temperature 446 °F | Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 85 | 85 | ASTM D785 |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
| Elongation at Break | >= 200 % | >= 200 % | ASTM D638 |
| Flexural Modulus | 1.135 GPa | 164.6 ksi | ASTM D790 |
| Izod Impact, Notched | 0.750 J/cm | 1.41 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ASTM D648 |