- 熔体流动速率 [g/10min]: 2.0
- 缺口冲击强度: 5.3
- 拉伸强度 [MPa]: 20.7
- 弯曲模量 [MPa]: 0.850
- 热变形温度 [℃]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Melt Flow | 2.0 - 4.0 g/10 min | 2.0 - 4.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
| Elongation at Break | >= 50 % | >= 50 % | ASTM D638 |
| Flexural Modulus | 0.850 GPa | 123 ksi | at 2 in/min; ASTM D790 |
| Izod Impact, Notched | 5.30 J/cm | 9.93 ft-lb/in | ASTM D256 |
| Gardner Impact | 17.0 J @Temperature -30.0 °C | 12.5 ft-lb @Temperature -22.0 °F | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ASTM D648 |