- 熔体流动速率 [g/10min]: 0.7
- 缺口冲击强度: 0.37
- 拉伸强度 [MPa]: 32.0
- 弯曲模量 [MPa]: 1.24
- 热变形温度 [℃]: 112.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 230 °C | 0.70 g/10 min @Load 4.76 lb, Temperature 446 °F | Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50 mm/min; ASTM D638 |
| Elongation at Yield | 8.0 % | 8.0 % | ASTM D638 |
| Flexural Modulus | 1.24 GPa | 180 ksi | 5 mm/min, tangent; ASTM D790 |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ASTM D648 |