- 熔体流动速率 [g/10min]: 18.0
- 缺口冲击强度: 0.267
- 拉伸强度 [MPa]: 35.0
- 弯曲模量 [MPa]: 1.31
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.905 g/cc | 0.905 g/cc | ASTM D792 |
| Melt Flow | 18 g/10 min @Load 2.16 kg, Temperature 230 °C | 18 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | 50 mm/min; ASTM D638 |
| Elongation at Yield | 9.0 % | 9.0 % | 50 mm/min; ASTM D638 |
| Tenacity | 0.256 N/tex | 2.90 g/denier | process conditions: draw ratios - 3.3, roll speed - 1250 m/min, spring temp - 225°, D 1000/68; ASTM D2556 |
| Flexural Modulus | 1.31 GPa | 190 ksi | ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm | 0.500 ft-lb/in | ASTM D256 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 164 °C | 327 °F | by DSC |