- 成型收缩率 [%]: 0.001
- 缺口冲击强度: 2.15
- 弯曲模量 [MPa]: 0.900
- 热变形温度 [℃]: 85.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm | 0.0010 - 0.0030 in/in @Thickness 0.126 in | 72 hr; ASTM D955 | ||
| 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm | 0.0020 - 0.0040 in/in @Thickness 0.126 in | 48 hr at 80°C; ASTM D955 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 67 | 67 | ASTM D2240 | ||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | 2 in/min; ASTM D638 | ||
| Elongation at Break | 15 % | 15 % | 2 in/min; ASTM D412 | ||
| Flexural Modulus | 0.900 GPa | 131 ksi | 1.3 mm/min at 70°C | ||
| 1.38 GPa | 200 ksi | 1.3 mm/min; ASTM D790 | |||
| Izod Impact, Notched | 2.15 J/cm | 4.03 ft-lb/in | ASTM D256 | ||
| Tear Strength | 100 kN/m | 571 pli | 2 in/min; ASTM D624 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 215 °C | 419 °F | DSC 10°C/min | ||
| Descriptive Properties | |||||
| Heat Sag | 8 mm | ASTM D3769, 1 hr at 80°C, 6 in. overhang | |||