- 密度 [g/cm3]: 1.68
- 弯曲模量 [MPa]: 17.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in³ | |||
| Filler Content | 47 % | 47 % | by volume | ||
| Thickness | 500 microns | 19.7 mil | laminate layer thickness | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 390 MPa | 56600 psi | transverse; ISO 527-4/5 | ||
| 400 MPa | 58000 psi | longitudinal; ISO 527-4/5 | |||
| Tensile Modulus | 20.1 GPa | 2920 ksi | transverse; ISO 527-4/5 | ||
| 20.5 GPa | 2970 ksi | longitudinal; ISO 527-4/5 | |||
| Flexural Strength | 365 MPa | 52900 psi | transverse; ISO 178 | ||
| 370 MPa | 53700 psi | longitudinal; ISO 178 | |||
| Flexural Modulus | 17.0 GPa | 2470 ksi | transverse; ISO 178 | ||
| 17.5 GPa | 2540 ksi | longitudinal; ISO 178 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 163 °C | 325 °F | DSC 3146 | ||
| Maximum Service Temperature, Air | 90.0 °C @Time 7.20e+7 sec | 194 °F @Time 20000 hour | Relative Temperature Index; IEC 216/1 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | ISO 75-1/2 | ||
| Minimum Service Temperature, Air | -10.0 °C | 14.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 190 - 210 °C | 374 - 410 °F | |||
| Descriptive Properties | |||||
| Reinforcement | Area weight | 600 g/m² | |||
| Fabric | twill 2/2 | ||||
| Fibers | roving glass | ||||
| Weight Rate | 50% longitudinal and transverse | ||||
| Yarn | 1200 tex longitudinal and transverse | ||||