- 熔体流动速率 [g/10min]: 10.0
- 密度 [g/cm3]: 0.907
- 拉伸强度 [MPa]: 29.5
- 硬度: 94.0
- 热变形温度 [℃]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.907 g/cc | 0.0328 lb/in³ | ISO 1183 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C | 10 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 94 | 94 | ISO 2039-2 |
| Tensile Strength, Yield | 29.5 MPa | 4280 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 13 % | 13 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.10 GPa | 160 ksi | At 1 mm/min; ISO 527-2 |
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ISO 75-2 |