Borealis GB364WG Polypropylene Compound, Glass Fiber Reinforced

Borealis GB364WG Polypropylene Compound, Glass Fiber Reinforced 物性表: Borealis GB364WG Polypropylene Compound, Glass Fiber Reinforced物性表及特性介绍,Borealis GB364WG Polypropylene Compound, Glass Fiber Reinforced注塑参数详情,如需Borealis GB364WG Polypropylene Compound, Glass Fiber Reinforced下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 2.0
  • 密度 [g/cm3]: 1.12
  • 缺口冲击强度: 8.5
  • 拉伸强度 [MPa]: 100.0
  • 弯曲模量 [MPa]: 6.00
  • 热变形温度 [℃]: 159.0
 
Physical PropertiesMetricEnglishComments
Density 1.12 g/cc0.0405 lb/in³ISO 1183
Linear Mold Shrinkage 0.0020 cm/cm0.0020 in/inaverage process; in flow; 150x80x2mm
 0.011 cm/cm0.011 in/inaverage process; cross flow; 150x80x2mm
Melt Flow 2.0 g/10 min
@Load 2.16 kg,
Temperature 230 °C
2.0 g/10 min
@Load 4.76 lb,
Temperature 446 °F
ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Ball Indentation Hardness 112 MPa16200 psi358 N/30s; ISO 2039
Tensile Strength, Yield 100 MPa14500 psiISO 527-2
Elongation at Break 3.3 %3.3 %50mm/min; ISO 527-2
Tensile Modulus 6.90 GPa1000 ksi1mm/min; ISO 527-2
Flexural Strength 135 MPa19600 psiISO 178
Flexural Modulus 6.00 GPa870 ksi2mm/min; ISO 178
Izod Impact, Notched (ISO)  8.50 kJ/m²
@Temperature -20.0 °C
4.04 ft-lb/in²
@Temperature -4.00 °F
ISO 180/1A
 11.0 kJ/m²
@Temperature 23.0 °C
5.23 ft-lb/in²
@Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched  4.90 J/cm²
@Temperature -20.0 °C
23.3 ft-lb/in²
@Temperature -4.00 °F
ISO 179/1eU
 5.80 J/cm²
@Temperature 23.0 °C
27.6 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched  0.900 J/cm²
@Temperature -20.0 °C
4.28 ft-lb/in²
@Temperature -4.00 °F
ISO 179/1eA
 1.20 J/cm²
@Temperature 23.0 °C
5.71 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eA
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 0.46 MPa (66 psi) 159 °C318 °FISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 143 °C289 °FISO 75-2
Vicat Softening Point  135 °C
@Load 5.10 kg
275 °F
@Load 11.2 lb
ISO 306
 164 °C
@Load 1.02 kg
327 °F
@Load 2.25 lb
ISO 306
 
Processing PropertiesMetricEnglishComments
Processing Temperature 230 - 280 °C446 - 536 °Fmass temperature
Feed Temperature 40.0 - 80.0 °C104 - 176 °F
Mold Temperature 30.0 - 50.0 °C86.0 - 122 °F
Injection Velocity 100 - 200 mm/sec3.94 - 7.87 in/sec
Hold Pressure 30.0 - 60.0 MPa4350 - 8700 psi
 
Descriptive Properties
Back Pressureas low as possible
Screw Speedlow to medium

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31602.html

免责声明: 本文 Borealis GB364WG Polypropylene Compound, Glass Fiber Reinforced 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4