- 熔体流动速率 [g/10min]: 125.0
- 密度 [g/cm3]: 0.905
- 缺口冲击强度: 1.6
- 拉伸强度 [MPa]: 35.0
- 弯曲模量 [MPa]: 1.55
- 热变形温度 [℃]: 91.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | Borealis Method; average process | ||
| Melt Flow | 125 g/10 min @Load 2.16 kg, Temperature 230 °C | 125 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 78.0 MPa | 11300 psi | 132 N/10s; ISO 2039 | ||
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Break | 15 % | 15 % | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 8.0 % | 8.0 % | 50mm/min; ISO 527-2 | ||
| Tensile Modulus | 1.60 GPa | 232 ksi | 1mm/min; ISO 527-2 | ||
| Flexural Strength | 45.0 MPa | 6530 psi | ISO 178 | ||
| Flexural Modulus | 1.55 GPa | 225 ksi | 2mm/min; ISO 178 | ||
| Izod Impact, Notched (ISO) | 1.60 kJ/m² @Temperature -20.0 °C | 0.761 ft-lb/in² @Temperature -4.00 °F | ISO 180/1A | ||
| 1.80 kJ/m² @Temperature 23.0 °C | 0.857 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | |||
| Charpy Impact Unnotched | 1.10 J/cm² @Temperature -20.0 °C | 5.23 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA | ||
| 5.50 J/cm² @Temperature 23.0 °C | 26.2 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Charpy Impact, Notched | 0.0800 J/cm² @Temperature -30.0 °C | 0.381 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.0900 J/cm² @Temperature -20.0 °C | 0.428 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA | |||
| 0.100 J/cm² @Temperature 23.0 °C | 0.476 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | -30°C/80°C; Borealis Method | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75-2 | ||
| Vicat Softening Point | 96.0 °C @Load 5.10 kg | 205 °F @Load 11.2 lb | ISO 306 | ||
| 153 °C @Load 1.02 kg | 307 °F @Load 2.25 lb | ISO 306 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 200 - 250 °C | 392 - 482 °F | mass temperature on double belt presses | ||
| 220 - 270 °C | 428 - 518 °F | mass temperature for direct LFT compression or injection molding | |||
| Mold Temperature | 30.0 - 60.0 °C | 86.0 - 140 °F | |||
| Descriptive Properties | |||||
| Injection Velocity | low to medium | ||||