- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 1.05
- 拉伸强度 [MPa]: 28.0
- 弯曲模量 [MPa]: 2.50
- 热变形温度 [℃]: 115.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | Borealis Method; average process | ||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C | 12 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| 49 g/10 min @Load 5.00 kg, Temperature 230 °C | 49 g/10 min @Load 11.0 lb, Temperature 446 °F | ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 62.0 MPa | 8990 psi | 358 N/30s; ISO 2039 | ||
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 5.0 % | 5.0 % | 50mm/min; ISO 527-2 | ||
| Flexural Modulus | 2.50 GPa | 363 ksi | 2mm/min; ISO 178 | ||
| Charpy Impact Unnotched | 2.56 J/cm² @Temperature -20.0 °C | 12.2 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eU | ||
| 5.20 J/cm² @Temperature 23.0 °C | 24.7 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.250 J/cm² @Temperature -20.0 °C | 1.19 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA | ||
| 0.600 J/cm² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ISO 75-2 | ||
| Vicat Softening Point | 153 °C @Load 1.02 kg | 307 °F @Load 2.25 lb | ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 220 - 260 °C | 428 - 500 °F | mass temperature | ||
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | |||
| Hold Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi | |||
| Descriptive Properties | |||||
| Back Pressure | low to medium | ||||
| Emission (µgC/g) | 18 | VDA 277 | |||
| Fogging (mg) | 0.97 | 100°C, 3h; DIN 75201 | |||
| 1 | 100°C, 16h; DIN 75201 | ||||
| Screw Speed | low to medium | ||||