- 熔体流动速率 [g/10min]: 3.3
- 密度 [g/cm3]: 1.16
- 缺口冲击强度: 16.0
- 拉伸强度 [MPa]: 65.0
- 弯曲模量 [MPa]: 5.10
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.00060 cm/cm | 0.00060 in/in | average process; in flow; 150x80x2mm | ||
| 0.00080 cm/cm | 0.00080 in/in | average process; cross flow; 150x80x2mm | |||
| Melt Flow | 3.3 g/10 min @Load 2.16 kg, Temperature 230 °C | 3.3 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | ISO 527-2 | ||
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527-2 | ||
| Tensile Modulus | 5.60 GPa | 812 ksi | 1mm/min; ISO 527-2 | ||
| Flexural Strength | 86.0 MPa | 12500 psi | ISO 178 | ||
| Flexural Modulus | 5.10 GPa | 740 ksi | 2mm/min; ISO 178 | ||
| Izod Impact, Notched (ISO) | 16.0 kJ/m² @Temperature -20.0 °C | 7.61 ft-lb/in² @Temperature -4.00 °F | ISO 180/1A | ||
| 28.0 kJ/m² @Temperature 23.0 °C | 13.3 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | |||
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature -20.0 °C | 28.6 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eU | ||
| 6.50 J/cm² @Temperature 23.0 °C | 30.9 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.30 J/cm² @Temperature -30.0 °C | 6.19 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 2.40 J/cm² @Temperature 23.0 °C | 11.4 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | ISO 75-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 230 - 280 °C | 446 - 536 °F | mass temperature | ||
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | |||
| Hold Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi | |||
| Descriptive Properties | |||||
| Back Pressure | as low as possible | ||||
| Screw Speed | low to medium | ||||