- 密度 [g/cm3]: 1.46
- 缺口冲击强度: 1.17
- 断裂伸长率 [%]: 133
- 弯曲强度 [MPa]: 100.0
- 弯曲模量 [MPa]: 10.5
- 热变形温度 [℃]: 246.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 - 1.85 g/cc | 0.0527 - 0.0668 lb/in³ | Average value: 1.55 g/cc Grade Count:10 |
| Filler Content | 15.0 - 20.0 % | 15.0 - 20.0 % | Average value: 18.8 % Grade Count:4 |
| Linear Mold Shrinkage | -0.00200 - 0.00400 cm/cm | -0.00200 - 0.00400 in/in | Average value: 0.00172 cm/cm Grade Count:9 |
| Linear Mold Shrinkage, Transverse | 0.00200 - 0.00900 cm/cm | 0.00200 - 0.00900 in/in | Average value: 0.00480 cm/cm Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 43.0 - 80.0 | 43.0 - 80.0 | Average value: 67.7 Grade Count:3 |
| Tensile Strength, Ultimate | 100 - 200 MPa | 14500 - 29000 psi | Average value: 161 MPa Grade Count:11 |
| Elongation at Break | 1.20 - 3.40 % | 1.20 - 3.40 % | Average value: 2.62 % Grade Count:10 |
| Modulus of Elasticity | 11.4 - 16.5 GPa | 1650 - 2400 ksi | Average value: 13.2 GPa Grade Count:9 |
| Flexural Yield Strength | 133 - 250 MPa | 19300 - 36300 psi | Average value: 195 MPa Grade Count:10 |
| Flexural Modulus | 10.5 - 14.5 GPa | 1520 - 2100 ksi | Average value: 11.9 GPa Grade Count:11 |
| Compressive Yield Strength | 82.0 - 85.0 MPa | 11900 - 12300 psi | Average value: 84.0 MPa Grade Count:3 |
| Compressive Modulus | 10.0 - 11.0 GPa | 1450 - 1600 ksi | Average value: 10.3 GPa Grade Count:3 |
| Izod Impact, Notched | 1.17 - 1.87 J/cm | 2.20 - 3.50 ft-lb/in | Average value: 1.49 J/cm Grade Count:4 |
| Izod Impact, Unnotched | 4.81 - 6.94 J/cm | 9.00 - 13.0 ft-lb/in | Average value: 5.61 J/cm Grade Count:4 |
| Izod Impact, Notched (ISO) | 2.00 - 45.0 kJ/m² | 0.952 - 21.4 ft-lb/in² | Average value: 30.8 kJ/m² Grade Count:6 |
| Izod Impact, Unnotched (ISO) | 15.0 - 101 kJ/m² | 7.14 - 48.1 ft-lb/in² | Average value: 59.5 kJ/m² Grade Count:4 |
| Charpy Impact Unnotched | 2.50 - 4.80 J/cm² | 11.9 - 22.8 ft-lb/in² | Average value: 4.03 J/cm² Grade Count:3 |
| Charpy Impact, Notched | 0.300 - 4.20 J/cm² | 1.43 - 20.0 ft-lb/in² | Average value: 2.93 J/cm² Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 - 1.00e+16 ohm-cm | 1.00e+12 - 1.00e+16 ohm-cm | Average value: 2.60e+15 ohm-cm Grade Count:5 |
| Surface Resistance | 1.00e+15 - 1.00e+17 ohm | 1.00e+15 - 1.00e+17 ohm | Average value: 2.08e+16 ohm Grade Count:5 |
| Dielectric Constant | 2.50 - 4.20 | 2.50 - 4.20 | Average value: 3.39 Grade Count:7 |
| Dielectric Strength | 25.6 - 34.0 kV/mm | 650 - 864 kV/in | Average value: 31.9 kV/mm Grade Count:5 |
| Dissipation Factor | 0.00300 - 0.0300 | 0.00300 - 0.0300 | Average value: 0.0158 Grade Count:7 |
| Arc Resistance | 135 sec | 135 sec | Average value: 135 sec Grade Count:3 |
| Comparative Tracking Index | 150 - 200 V | 150 - 200 V | Average value: 188 V Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | -3.00 - 23.0 µm/m-°C | -1.67 - 12.8 µin/in-°F | Average value: 7.40 µm/m-°C Grade Count:4 |
| CTE, linear, Transverse to Flow | 18.0 - 66.0 µm/m-°C | 10.0 - 36.7 µin/in-°F | Average value: 41.6 µm/m-°C Grade Count:4 |
| Melting Point | 280 - 336 °C | 536 - 637 °F | Average value: 306 °C Grade Count:7 |
| Deflection Temperature at 0.46 MPa (66 psi) | 246 - 298 °C | 475 - 568 °F | Average value: 261 °C Grade Count:4 |
| Deflection Temperature at 1.8 MPa (264 psi) | 197 - 304 °C | 387 - 580 °F | Average value: 248 °C Grade Count:11 |
| Deflection Temperature at 8.0 MPa | 119 - 157 °C | 246 - 315 °F | Average value: 144 °C Grade Count:3 |
| Vicat Softening Point | 162 - 202 °C | 324 - 396 °F | Average value: 177 °C Grade Count:4 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:8 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 120 °C | 68.0 - 248 °F | Average value: 62.5 °C Grade Count:4 |
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Average value: 65.0 °C Grade Count:4 |
| Die Temperature | 290 - 350 °C | 554 - 662 °F | Average value: 318 °C Grade Count:4 |
| Melt Temperature | 209 - 399 °C | 408 - 750 °F | Average value: 310 °C Grade Count:10 |
| Mold Temperature | 37.8 - 121 °C | 100 - 250 °F | Average value: 83.5 °C Grade Count:9 |
| Injection Velocity | 150 mm/sec | 5.91 in/sec | Average value: 150 mm/sec Grade Count:3 |
| Drying Temperature | 149 - 150 °C | 300 - 302 °F | Average value: 149 °C Grade Count:8 |
| Dry Time | 3.00 - 8.00 hour | 3.00 - 8.00 hour | Average value: 5.88 hour Grade Count:8 |
| Moisture Content | 0.0100 % | 0.0100 % | Average value: 0.0100 % Grade Count:4 |
| Dew Point | -40.0 - -28.9 °C | -40.0 - -20.0 °F | Average value: -34.4 °C Grade Count:6 |
| Injection Pressure | 34.5 - 150 MPa | 5000 - 21800 psi | Average value: 95.2 MPa Grade Count:8 |
| Hold Pressure | 48.0 - 150 MPa | 6960 - 21800 psi | Average value: 80.7 MPa Grade Count:4 |
| Back Pressure | 3.00 MPa | 435 psi | Average value: 3.00 MPa Grade Count:4 |
| Screw Speed | 80.0 - 200 rpm | 80.0 - 200 rpm | Average value: 140 rpm Grade Count:3 |
| Hot-Working Temperature | 285 - 345 °C | 545 - 653 °F | Average value: 307 °C Grade Count:3 |