  4. Celanese Zenite® 5145L BK010 LCP

Celanese Zenite® 5145L BK010 LCP

Celanese Zenite® 5145L BK010 LCP 物性表: Celanese Zenite® 5145L BK010 LCP物性表及特性介绍,Celanese Zenite® 5145L BK010 LCP注塑参数详情,如需Celanese Zenite® 5145L BK010 LCP下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.75
  • 缺口冲击强度: 2.5
  • 弯曲强度 [MPa]: 130.0
  • 弯曲模量 [MPa]: 11.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.76 g/cc1.76 g/ccASTM D 792
Density 1.75 g/cc0.0632 lb/in³ISO 1183
Filler Content 45 %45 %
Linear Mold Shrinkage, Flow 0.00090 cm/cm
@Thickness 2.00 mm		0.00090 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0050 cm/cm
@Thickness 2.00 mm		0.0050 in/in
@Thickness 0.0787 in		ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 115 MPa16700 psiISO 527
Tensile Strength, Ultimate 130 MPa
@Temperature 23.0 °C		18900 psi
@Temperature 73.4 °F		ASTM D 638
Elongation at Break 3.1 %3.1 %ISO 527
 3.3 %
@Temperature 23.0 °C		3.3 %
@Temperature 73.4 °F		ASTM D 638
Tensile Modulus 15.0 GPa
@Temperature 23.0 °C		2180 ksi
@Temperature 73.4 °F		ISO 527
Flexural Strength  160 MPa
@Temperature 23.0 °C		23200 psi
@Temperature 73.4 °F		ASTM D 790
 190 MPa
@Temperature 23.0 °C		27600 psi
@Temperature 73.4 °F		ISO 178
Flexural Modulus  11.0 GPa
@Temperature 23.0 °C		1600 ksi
@Temperature 73.4 °F		ISO 178
 13.0 GPa
@Temperature 23.0 °C		1890 ksi
@Temperature 73.4 °F		ASTM D 790
Izod Impact, Notched 2.50 J/cm
@Temperature 23.0 °C		4.68 ft-lb/in
@Temperature 73.4 °F		ASTM D 256
Izod Impact, Unnotched 6.00 J/cm
@Temperature 23.0 °C		11.2 ft-lb/in
@Temperature 73.4 °F		ASTM D 4812
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 1.00e+15 ohm-cm1.00e+15 ohm-cmASTM D 257
Surface Resistance 1.00e+15 ohm1.00e+15 ohmASTM D 257
Dielectric Constant  3.4
@Frequency 1000 Hz,
Temperature 23.0 °C		3.4
@Frequency 1000 Hz,
Temperature 73.4 °F		ASTM D 150
 3.9
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.9
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		ASTM D 150
 4.4
@Frequency 100000 Hz,
Temperature 23.0 °C		4.4
@Frequency 100000 Hz,
Temperature 73.4 °F		ASTM D 150
 4.5
@Frequency 10000 Hz,
Temperature 23.0 °C		4.5
@Frequency 10000 Hz,
Temperature 73.4 °F		ASTM D 150
 4.7
@Frequency 1.00e+9 Hz,
Temperature 23.0 °C		4.7
@Frequency 1.00e+9 Hz,
Temperature 73.4 °F		2.0mm; ASTM D 2520 B
 4.8
@Frequency 1.00e+10 Hz,
Temperature 23.0 °C		4.8
@Frequency 1.00e+10 Hz,
Temperature 73.4 °F		2.0mm; ASTM D 2520 B
 5.0
@Frequency 2.00e+10 Hz,
Temperature 23.0 °C		5.0
@Frequency 2.00e+10 Hz,
Temperature 73.4 °F		2.0mm; ASTM D 2520 B
Dielectric Strength 22.0 kV/mm
@Temperature 23.0 °C		559 kV/in
@Temperature 73.4 °F		500 V/s, Short Time; ASTM D 149
 24.0 kV/mm
@Thickness 2.00 mm,
Temperature 150 °C		610 kV/in
@Thickness 0.0787 in,
Temperature 302 °F		IEC 60243-1
 24.0 kV/mm
@Thickness 2.00 mm,
Temperature 200 °C		610 kV/in
@Thickness 0.0787 in,
Temperature 392 °F		IEC 60243-1
 27.0 kV/mm
@Thickness 2.00 mm,
Temperature 100 °C		686 kV/in
@Thickness 0.0787 in,
Temperature 212 °F		IEC 60243-1
 35.0 kV/mm
@Thickness 1.00 mm,
Temperature 200 °C		889 kV/in
@Thickness 0.0394 in,
Temperature 392 °F		IEC 60243-1
 40.0 kV/mm
@Thickness 1.00 mm,
Temperature 150 °C		1020 kV/in
@Thickness 0.0394 in,
Temperature 302 °F		IEC 60243-1
 40.0 kV/mm
@Thickness 1.00 mm,
Temperature 100 °C		1020 kV/in
@Thickness 0.0394 in,
Temperature 212 °F		IEC 60243-1
 45.0 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		1140 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		IEC 60243-1
Dissipation Factor  0.014
@Frequency 10000 Hz		0.014
@Frequency 10000 Hz		ASTM D 150
 0.017
@Frequency 1000 Hz		0.017
@Frequency 1000 Hz		ASTM D 150
 0.018
@Frequency 100000 Hz		0.018
@Frequency 100000 Hz		ASTM D 150
 0.018
@Frequency 1.00e+6 Hz		0.018
@Frequency 1.00e+6 Hz		ASTM D 150
 0.0060
@Thickness 2.00 mm,
Frequency 1.00e+9 Hz		0.0060
@Thickness 0.0787 in,
Frequency 1.00e+9 Hz		ASTM D2520 B
 0.0060
@Thickness 2.00 mm,
Frequency 1.00e+10 Hz		0.0060
@Thickness 0.0787 in,
Frequency 1.00e+10 Hz		ASTM D2520 B
 0.0080
@Thickness 2.00 mm,
Frequency 2.00e+10 Hz		0.0080
@Thickness 0.0787 in,
Frequency 2.00e+10 Hz		ASTM D2520 B
Comparative Tracking Index 175 V175 VIEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear  -1.00 µm/m-°C
@Thickness 2.00 mm,
Temperature 160 - 260 °C		-0.556 µin/in-°F
@Thickness 0.0787 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
 0.000 µm/m-°C
@Thickness 4.00 mm,
Temperature 160 - 260 °C		0.000 µin/in-°F
@Thickness 0.157 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
 4.00 µm/m-°C
@Thickness 2.00 mm,
Temperature -40.0 - 23.0 °C		2.22 µin/in-°F
@Thickness 0.0787 in,
Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 4.00 µm/m-°C
@Thickness 4.00 mm,
Temperature -40.0 - 23.0 °C		2.22 µin/in-°F
@Thickness 0.157 in,
Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 4.00 µm/m-°C
@Thickness 2.00 mm,
Temperature -40.0 - 260 °C		2.22 µin/in-°F
@Thickness 0.0787 in,
Temperature -40.0 - 500 °F		ISO 11359-1/-2
 4.00 µm/m-°C
@Thickness 4.00 mm,
Temperature -40.0 - 260 °C		2.22 µin/in-°F
@Thickness 0.157 in,
Temperature -40.0 - 500 °F		ISO 11359-1/-2
 4.00 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		2.22 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 5.00 µm/m-°C
@Thickness 4.00 mm,
Temperature 23.0 - 55.0 °C		2.78 µin/in-°F
@Thickness 0.157 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 6.00 µm/m-°C
@Thickness 2.00 mm,
Temperature 55.0 - 160 °C		3.33 µin/in-°F
@Thickness 0.0787 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 7.00 µm/m-°C
@Thickness 4.00 mm,
Temperature 55.0 - 160 °C		3.89 µin/in-°F
@Thickness 0.157 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  52.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		28.9 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2; 2mm
 52.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		28.9 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2; 4mm
 77.0 µm/m-°C
@Temperature -40.0 - 260 °C		42.8 µin/in-°F
@Temperature -40.0 - 500 °F		ISO 11359-1/-2; 2mm
 80.0 µm/m-°C
@Temperature -40.0 - 260 °C		44.4 µin/in-°F
@Temperature -40.0 - 500 °F		ISO 11359-1/-2; 4mm
 60.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		33.3 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 60.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 23.0 - 55.0 °C		33.3 µin/in-°F
@Thickness 0.157 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 80.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 55.0 - 160 °C		44.4 µin/in-°F
@Thickness 0.0787 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 80.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 55.0 - 160 °C		44.4 µin/in-°F
@Thickness 0.157 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 95.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 160 - 260 °C		52.8 µin/in-°F
@Thickness 0.0787 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
 100 µm/m-°C
@Thickness 4.00 mm,
Temperature 160 - 260 °C		55.6 µin/in-°F
@Thickness 0.157 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
Melting Point 319 °C606 °F10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 275 °C527 °FASTM D 648
 290 °C554 °FISO 75-1/-2 1993/N2
UL RTI, Electrical 130 °C
@Thickness 0.800 mm		266 °F
@Thickness 0.0315 in		UL 746B
UL RTI, Mechanical with Impact 130 °C
@Thickness 0.800 mm		266 °F
@Thickness 0.0315 in		UL 746B
UL RTI, Mechanical without Impact 130 °C
@Thickness 0.800 mm		266 °F
@Thickness 0.0315 in		UL 746B
Flammability, UL94  V-0
@Thickness 0.800 mm		V-0
@Thickness 0.0315 in		IEC 60695-11-10
 V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		IEC 60695-11-10
 V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		UL94
 V-0
@Thickness 0.800 mm		V-0
@Thickness 0.0315 in		UL94
 V-0
@Thickness 3.00 mm		V-0
@Thickness 0.118 in		UL94
 V-0
@Thickness 3.00 mm		V-0
@Thickness 0.118 in		IEC 60695-11-10
Glow Wire Test  800 °C
@Thickness 2.00 mm		1470 °F
@Thickness 0.0787 in		Glow Wire Ignition Temperature; IEC 60695-2-13
 800 °C
@Thickness 3.00 mm		1470 °F
@Thickness 0.118 in		Glow Wire Ignition Temperature; IEC 60695-2-13
 960 °C
@Thickness 2.00 mm		1760 °F
@Thickness 0.0787 in		Glow Wire Flammability Index; IEC 60695-2-12
 960 °C
@Thickness 3.00 mm		1760 °F
@Thickness 0.118 in		Glow Wire Flammability Index; IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 335 °C635 °FOptimum
 325 - 345 °C617 - 653 °F
Mold Temperature 80.0 °C176 °FOptimum
 40.0 - 150 °C104 - 302 °F
Drying Temperature 150 °C302 °F
Dry Time 3 hour3 hourDehumidified Dryer
Moisture Content <= 0.010 %<= 0.010 %
 
Descriptive Properties
ColorBlack
Drying RecommendedYes
FillerGlass Reinforced
FormsPellets
GenericLCP
Part Marking Code>LCP-GF45<ISO 11469
Polymer FamilyLCP
Polymer TypeLCP
Processing MethodInjection Molding
Product CategoryElectrical Resins
 Flame Retardant Resins
 Glass Reinforced Resins
Region AvailableAmericas
 Asia/Pacific
 Europe
Resin IdentificationLCP-GF45ISO 1043

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31761.html

免责声明: 本文 Celanese Zenite® 5145L BK010 LCP 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4