  4. Celanese Zenite® ZE55801 NC010 LCP

Celanese Zenite® ZE55801 NC010 LCP

Celanese Zenite® ZE55801 NC010 LCP 物性表: Celanese Zenite® ZE55801 NC010 LCP物性表及特性介绍,Celanese Zenite® ZE55801 NC010 LCP注塑参数详情,如需Celanese Zenite® ZE55801 NC010 LCP下载, 可到相关下载区下载
  • 缺口冲击强度: 3.45
  • 弯曲强度 [MPa]: 140.0
  • 弯曲模量 [MPa]: 11.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.65 g/cc1.65 g/ccASTM D 792
Filler Content 30 %30 %
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength, Ultimate 140 MPa
@Temperature 23.0 °C		20300 psi
@Temperature 73.4 °F		ASTM D 638
Elongation at Break 4.0 %
@Temperature 23.0 °C		4.0 %
@Temperature 73.4 °F		ASTM D 638
Flexural Strength 150 MPa21800 psiASTM D 790
Flexural Modulus 11.0 GPa
@Temperature 23.0 °C		1600 ksi
@Temperature 73.4 °F		ASTM D 790
Izod Impact, Notched 3.45 J/cm
@Temperature 23.0 °C		6.46 ft-lb/in
@Temperature 73.4 °F		ASTM D 256
Izod Impact, Unnotched 8.58 J/cm
@Temperature 23.0 °C		16.1 ft-lb/in
@Temperature 73.4 °F		ASTM D 4812
 
Electrical PropertiesMetricEnglishComments
Comparative Tracking Index 150 V150 VIEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear  -4.00 µm/m-°C
@Thickness 2.00 mm,
Temperature 160 - 260 °C		-2.22 µin/in-°F
@Thickness 0.0787 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
 -4.00 µm/m-°C
@Thickness 4.00 mm,
Temperature 160 - 260 °C		-2.22 µin/in-°F
@Thickness 0.157 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
 1.00 µm/m-°C
@Thickness 2.00 mm,
Temperature -40.0 - 260 °C		0.556 µin/in-°F
@Thickness 0.0787 in,
Temperature -40.0 - 500 °F		ISO 11359-1/-2
 2.00 µm/m-°C
@Thickness 2.00 mm,
Temperature -40.0 - 23.0 °C		1.11 µin/in-°F
@Thickness 0.0787 in,
Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 2.00 µm/m-°C
@Thickness 4.00 mm,
Temperature -40.0 - 23.0 °C		1.11 µin/in-°F
@Thickness 0.157 in,
Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 2.00 µm/m-°C
@Thickness 4.00 mm,
Temperature -40.0 - 260 °C		1.11 µin/in-°F
@Thickness 0.157 in,
Temperature -40.0 - 500 °F		ISO 11359-1/-2
 3.00 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		1.67 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 3.00 µm/m-°C
@Thickness 4.00 mm,
Temperature 23.0 - 55.0 °C		1.67 µin/in-°F
@Thickness 0.157 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 3.00 µm/m-°C
@Thickness 2.00 mm,
Temperature 55.0 - 160 °C		1.67 µin/in-°F
@Thickness 0.0787 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 4.00 µm/m-°C
@Thickness 4.00 mm,
Temperature 55.0 - 160 °C		2.22 µin/in-°F
@Thickness 0.157 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  58.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		32.2 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2; 2mm
 60.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		33.3 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2; 4mm
 85.0 µm/m-°C
@Temperature -40.0 - 260 °C		47.2 µin/in-°F
@Temperature -40.0 - 500 °F		ISO 11359-1/-2; 2mm
 88.0 µm/m-°C
@Temperature -40.0 - 260 °C		48.9 µin/in-°F
@Temperature -40.0 - 500 °F		ISO 11359-1/-2; 4mm
 66.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		36.7 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 69.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 23.0 - 55.0 °C		38.3 µin/in-°F
@Thickness 0.157 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 88.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 55.0 - 160 °C		48.9 µin/in-°F
@Thickness 0.0787 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 91.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 55.0 - 160 °C		50.6 µin/in-°F
@Thickness 0.157 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 105 µm/m-°C
@Thickness 2.00 mm,
Temperature 160 - 260 °C		58.3 µin/in-°F
@Thickness 0.0787 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
 110 µm/m-°C
@Thickness 4.00 mm,
Temperature 160 - 260 °C		61.1 µin/in-°F
@Thickness 0.157 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 260 °C500 °FISO 75-1/-2
UL RTI, Electrical 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
UL RTI, Mechanical with Impact 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
UL RTI, Mechanical without Impact 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
Flammability, UL94  V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		IEC 60695-11-10
 V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		UL94
 
Processing PropertiesMetricEnglishComments
Melt Temperature 335 °C635 °FOptimum
 330 - 350 °C626 - 662 °F
Mold Temperature 80.0 °C176 °FOptimum
 40.0 - 150 °C104 - 302 °F
Drying Temperature 150 °C302 °F
Dry Time 3 hour3 hourDehumidified Dryer
Moisture Content <= 0.010 %<= 0.010 %
 
Descriptive Properties
ColorNatural
Drying RecommendedYes
FillerGlass Reinforced
FormsPellets
GenericLCP
Part Marking Code>LCP-GF30<ISO 11469
Polymer FamilyLCP
Polymer TypeLCP
Processing MethodInjection Molding
Product CategoryElectrical Resins
 Glass Reinforced Resins
Region AvailableAmericas
 Asia/Pacific
 Europe
Resin IdentificationLCP-GF30ISO 1043

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31787.html

免责声明: 本文 Celanese Zenite® ZE55801 NC010 LCP 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络