- 密度 [g/cm3]: 1.79
- 缺口冲击强度: 3.0
- 弯曲模量 [MPa]: 9.00
- 热变形温度 [℃]: 255.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.79 g/cc | 0.0647 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.00400 cm/cm | 0.00400 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0120 cm/cm | 0.0120 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 90.0 MPa | 13100 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 3.20 % | 3.20 % | Flexural strain; ISO 178 | ||
| 3.60 % | 3.60 % | 5mm/min; ISO 527-2/1A | |||
| Tensile Modulus | 8.00 GPa | 1160 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 | ||
| Flexural Modulus | 9.00 GPa | 1310 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 27.0 kJ/m² | 12.8 ft-lb/in² | ISO 180/1U | ||
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Dissipation Factor | 0.0163 @Frequency 1.00e+6 Hz | 0.0163 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 23.0 µm/m-°C | 12.8 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 49.0 µm/m-°C | 27.2 µin/in-°F | ISO 11359-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-1, -2 | ||
| Flammability, UL94 | V-0 | V-0 | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 30.0 °C | 68.0 - 86.0 °F | |||
| 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | |||
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Zone 1 | 315 - 325 °C | 599 - 617 °F | |||
| Zone 2 | 320 - 330 °C | 608 - 626 °F | |||
| Zone 3 | 325 - 335 °C | 617 - 635 °F | |||
| Zone 4 | 330 - 340 °C | 626 - 644 °F | |||
| Die Temperature | 335 - 345 °C | 635 - 653 °F | |||
| Melt Temperature | 335 - 345 °C | 635 - 653 °F | |||
| 340 °C | 644 °F | Injection molding; ISO 294 | |||
| Mold Temperature | 100 °C | 212 °F | Injection molding; ISO 294 | ||
| Injection Velocity | 150 mm/sec | 5.91 in/sec | ISO 294 | ||
| Drying Temperature | 170 °C | 338 °F | |||
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |||
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual | ||
| Dew Point | <= -40.0 °C | <= -40.0 °F | Pre-drying | ||
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Hold Pressure | 69.0 MPa | 10000 psi | ISO 294 | ||
| 50.0 - 150 MPa | 7250 - 21800 psi | ||||
| Back Pressure | 3.00 MPa | 435 psi | |||
| Screw Speed | 80.0 rpm @Diameter 40.0 mm | 80.0 rpm @Diameter 1.57 in | |||
| 140 rpm @Diameter 25.0 mm | 140 rpm @Diameter 0.984 in | ||||
| 200 rpm @Diameter 16.0 mm | 200 rpm @Diameter 0.630 in | ||||
| Hot-Working Temperature | 335 - 345 °C | 635 - 653 °F | |||
| Descriptive Properties | |||||
| Injection speed | very fast | ||||
| Longer pre-drying times/storage | 100° C. | <= 60 h | |||
| mold temperature | 120 - 140°C (For MID applications ) | ||||