- 密度 [g/cm3]: 1.67
- 缺口冲击强度: 12.0
- 弯曲模量 [MPa]: 14.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.00400 cm/cm | 0.00400 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.00600 cm/cm | 0.00600 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 140 MPa | 20300 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 1.30 % | 1.30 % | 5mm/min; ISO 527-2/1A | ||
| 2.00 % | 2.00 % | Flexural strain; ISO 178 | |||
| Flexural Strength | 230 MPa | 33400 psi | ISO 178 | ||
| Flexural Modulus | 14.5 GPa | 2100 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ISO 180/1U | ||
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | IEC 60093 | ||
| Dielectric Constant | 3.50 @Frequency 1.00e+6 Hz | 3.50 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dielectric Strength | 37.0 kV/mm | 940 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.00900 @Frequency 1.00e+6 Hz | 0.00900 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 1.00 µm/m-°C | 0.556 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 23.0 µm/m-°C | 12.8 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 350 °C | 662 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 340 °C | 644 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 8.0 MPa | 267 °C | 513 °F | ISO 75-1, -2 | ||
| Flammability, UL94 | V-0 | V-0 | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 30.0 °C | 68.0 - 86.0 °F | |||
| 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | |||
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Zone 1 | 350 - 360 °C | 662 - 680 °F | |||
| Zone 2 | 355 - 365 °C | 671 - 689 °F | |||
| Zone 3 | 360 - 370 °C | 680 - 698 °F | |||
| Zone 4 | 365 - 375 °C | 689 - 707 °F | |||
| Die Temperature | 370 - 380 °C | 698 - 716 °F | |||
| Melt Temperature | 370 - 380 °C | 698 - 716 °F | |||
| Drying Temperature | 150 - 170 °C | 302 - 338 °F | |||
| Dry Time | 6.00 hour | 6.00 hour | |||
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual | ||
| Dew Point | <= -40.0 °C | <= -40.0 °F | Pre-drying | ||
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Hold Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Back Pressure | 3.00 MPa | 435 psi | |||
| Screw Speed | 80.0 rpm @Diameter 40.0 mm | 80.0 rpm @Diameter 1.57 in | |||
| 140 rpm @Diameter 25.0 mm | 140 rpm @Diameter 0.984 in | ||||
| 200 rpm @Diameter 16.0 mm | 200 rpm @Diameter 0.630 in | ||||
| Hot-Working Temperature | 360 - 370 °C | 680 - 698 °F | |||
| Descriptive Properties | |||||
| Injection speed | very fast | ||||
| Longer pre-drying times/storage | 100° C. | <= 60 h | |||
| Short metering strokes | accumulator is recommended | to get short injection times | |||