- 密度 [g/cm3]: 1.6
- 缺口冲击强度: 20.0
- 弯曲模量 [MPa]: 16.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 74 | 74 | ISO 2039-2 |
| Tensile Strength at Break | 170 MPa | 24700 psi | 5 mm/min; ISO 527-2/1A |
| Elongation at Break | 1.5 % | 1.5 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 16.5 GPa | 2390 ksi | 1 mm/min; ISO 527-2/1A |
| Flexural Strength | 245 MPa | 35500 psi | ISO 178 |
| Flexural Modulus | 16.4 GPa | 2380 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 27.0 kJ/m² | 12.8 ft-lb/in² | ISO 180/1U |
| Charpy Impact Unnotched | 2.90 J/cm² | 13.8 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 2.40 J/cm² | 11.4 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 100 Hz | 4.0 @Frequency 100 Hz | IEC 60250 |
| 5.6 @Frequency 1e+6 Hz | 5.6 @Frequency 1e+6 Hz | IEC 60250 | |
| Dielectric Strength | 39.0 kV/mm | 991 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.020 @Frequency 100 Hz | 0.020 @Frequency 100 Hz | IEC 60250 |
| 0.0221 @Frequency 1e+6 Hz | 0.0221 @Frequency 1e+6 Hz | IEC 60250 | |
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 2.00 µm/m-°C @Temperature 20.0 °C | 1.11 µin/in-°F @Temperature 68.0 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 22.0 µm/m-°C @Temperature 20.0 °C | 12.2 µin/in-°F @Temperature 68.0 °F | ISO 11359-2 |
| Melting Point | 330 °C | 626 °F | ISO 11357-1,2,3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 298 °C | 568 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 233 °C | 451 °F | ISO 75-1, -2 |
| Vicat Softening Point | 221 °C | 430 °F | ISO 306 |
| Flammability, UL94 | V-0 | V-0 | thickness h |
| Oxygen Index | 50 % | 50 % | ISO 4589 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 315 - 325 °C | 599 - 617 °F | |
| Middle Barrel Temperature | 325 - 335 °C | 617 - 635 °F | |
| Front Barrel Temperature | 330 - 340 °C | 626 - 644 °F | |
| Nozzle Temperature | 335 - 345 °C | 635 - 653 °F | |
| Melt Temperature | 335 - 345 °C | 635 - 653 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |