- 密度 [g/cm3]: 1.6
- 缺口冲击强度: 25.0
- 弯曲模量 [MPa]: 15.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 60 | 60 | ISO 2039-2 |
| Tensile Strength at Break | 140 MPa | 20300 psi | 5 mm/min; ISO 527-2/1A |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527-2/1A |
| Tensile Modulus | 16.0 GPa | 2320 ksi | 1 mm/min; ISO 527-2/1A |
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 |
| Flexural Modulus | 15.4 GPa | 2230 ksi | ISO 178 |
| Compressive Yield Strength | 94.0 MPa | 13600 psi | at 1% strain; ISO 604 |
| Compressive Modulus | 14.0 GPa | 2030 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | ISO 180/1U |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.6 @Frequency 1e+6 Hz | 3.6 @Frequency 1e+6 Hz | IEC 60250 |
| Dielectric Strength | 56.0 kV/mm | 1420 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.029 @Frequency 1e+6 Hz | 0.029 @Frequency 1e+6 Hz | IEC 60250 |
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 3.00 µm/m-°C @Temperature 20.0 °C | 1.67 µin/in-°F @Temperature 68.0 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 19.0 µm/m-°C @Temperature 20.0 °C | 10.6 µin/in-°F @Temperature 68.0 °F | ISO 11359-2 |
| Melting Point | 370 °C | 698 °F | ISO 11357-1,2,3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 300 °C | 572 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 244 °C | 471 °F | ISO 75-1, -2 |
| Vicat Softening Point | 226 °C | 439 °F | ISO 306 |
| Flammability, UL94 | V-0 | V-0 | thickness h |
| Oxygen Index | 50 % | 50 % | ISO 4589 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 355 - 365 °C | 671 - 689 °F | |
| Middle Barrel Temperature | 360 - 370 °C | 680 - 698 °F | |
| Front Barrel Temperature | 360 - 370 °C | 680 - 698 °F | |
| Nozzle Temperature | 355 - 365 °C | 671 - 689 °F | |
| Melt Temperature | 365 - 370 °C | 689 - 698 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |