- 密度 [g/cm3]: 1.44
- 吸水率 [%]: 0.01
- 缺口冲击强度: 0.7
- 拉伸强度 [MPa]: 95.1
- 弯曲强度 [MPa]: 95.1
- 热变形温度 [℃]: 263.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ASTM Data |
| Water Absorption | 0.010 % | 0.010 % | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 95.1 MPa | 13800 psi | ASTM Data |
| Tensile Strength, Yield | 95.1 MPa | 13800 psi | ASTM Data |
| Tensile Modulus | 9.65 GPa | 1400 ksi | ASTM Data |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | ASTM Data |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 23.6 kV/mm | 599 kV/in | |
| Dissipation Factor | 0.0010 | 0.0010 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 30.5 µm/m-°C @Temperature 20.0 °C | 16.9 µin/in-°F @Temperature 68.0 °F | ASTM data |
| Deflection Temperature at 0.46 MPa (66 psi) | 263 °C | 505 °F | Unannealed; ASTM Data |
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | Unannealed; ASTM Data |
| Vicat Softening Point | 263 °C | 505 °F | |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | |