- 密度 [g/cm3]: 1.08
- 热变形温度 [℃]: 82.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 - 1.38 g/cc | 0.0390 - 0.0498 lb/in³ | |
| Viscosity | 2300 - 2900 cP @Shear Rate 1.00 1/s, Temperature 25.0 °C | 2300 - 2900 cP @Shear Rate 1.00 1/s, Temperature 77.0 °F | LVF#4, Uncured |
| Viscosity Measurement | 4.5 - 6.5 | 4.5 - 6.5 | Thix Index, Uncured |
| Mechanical Properties | Metric | English | Comments |
| Elongation at Break | 1.7 - 2.2 % | 1.7 - 2.2 % | Flex; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 82.2 - 98.9 °C | 180 - 210 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 25.0 °C | 77.0 °F | 40 - 60 minute film cure |
| Gel Time | 8.00 - 12.0 min @Temperature 25.0 °C | 8.00 - 12.0 min @Temperature 77.0 °F | |