- 密度 [g/cm3]: 1.82
- 吸水率 [%]: 0.15
- 缺口冲击强度: 7.28
- 弯曲模量 [MPa]: 20.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.250 g/cc | 0.00903 lb/in³ | ASTM D1895 | ||
| Density | 1.82 g/cc | 0.0658 lb/in³ | ASTM D792 | ||
| Water Absorption | 0.15 % @Temperature 50.0 °C, Time 173000 sec | 0.15 % @Temperature 122 °F, Time 48.0 hour | ASTM D570 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 105 | 105 | ASTM D2583 | ||
| Tensile Strength at Break | 94.0 MPa | 13600 psi | ASTM D638 | ||
| Flexural Strength | 235 MPa | 34100 psi | at rupture; ASTM D790 | ||
| Flexural Modulus | 20.0 GPa | 2900 ksi | ASTM D790 | ||
| Compressive Strength | 203 MPa | 29400 psi | ASTM D695 | ||
| Izod Impact, Notched | 7.28 J/cm | 13.6 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz | 3.7 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Dielectric Strength | 15.0 kV/mm @Frequency 60.0 Hz | 381 kV/in @Frequency 60.0 Hz | step-by-step, wet; ASTM D149 | ||
| 15.4 kV/mm @Frequency 60.0 Hz | 391 kV/in @Frequency 60.0 Hz | step-by-step, dry; ASTM D149 | |||
| 17.0 kV/mm @Frequency 60.0 Hz | 432 kV/in @Frequency 60.0 Hz | short time, wet; ASTM D149 | |||
| 17.4 kV/mm @Frequency 60.0 Hz | 442 kV/in @Frequency 60.0 Hz | short time, dry; ASTM D149 | |||
| Dissipation Factor | 0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Arc Resistance | 125 sec | 125 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 282 °C | >= 540 °F | As Molded; ASTM D648A | ||
| >= 282 °C | >= 540 °F | Post Baked; ASTM D648A | |||
| Shrinkage | 0.090 % | 0.090 % | Post Shrinkage; ASTM D955 | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Form | Coarse Flake | ||||
| Molding Method | Compression | ||||
| Transfer | |||||