- 密度 [g/cm3]: 1.7
- 吸水率 [%]: 0.11
- 缺口冲击强度: 0.31
- 弯曲模量 [MPa]: 11.7
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | ASTM D792 | ||
| Water Absorption | 0.11 % @Temperature 50.0 °C, Time 173000 sec | 0.11 % @Temperature 122 °F, Time 48.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ASTM D638 | ||
| Flexural Strength | 123 MPa | 17800 psi | at rupture; ASTM D790 | ||
| Flexural Modulus | 11.7 GPa | 1700 ksi | ASTM D790 | ||
| Compressive Strength | 220 MPa | 31900 psi | ASTM D695 | ||
| Izod Impact, Notched | 0.310 J/cm | 0.581 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz | 3.7 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Dielectric Strength | 12.8 kV/mm @Frequency 60.0 Hz | 325 kV/in @Frequency 60.0 Hz | step-by-step, wet; ASTM D149 | ||
| 13.3 kV/mm @Frequency 60.0 Hz | 338 kV/in @Frequency 60.0 Hz | short time, wet; ASTM D149 | |||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Arc Resistance | 190 sec | 190 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 32.0 µm/m-°C | 17.8 µin/in-°F | ASTM E831 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Form | Granular | ||||
| Molding Method | Compression | ||||
| Transfer | |||||