- 弯曲模量 [MPa]: 3.03
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Viscosity | 1500 cP | 1500 cP | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 95 | 95 | |
| Tensile Strength at Break | 61.4 MPa | 8900 psi | |
| Elongation at Break | 7.6 % | 7.6 % | |
| Flexural Strength | 100 MPa | 14500 psi | |
| Flexural Modulus | 3.03 GPa | 440 ksi | |
| Compressive Strength | 279 MPa | 40500 psi | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.51e+15 ohm-cm | 1.51e+15 ohm-cm | C 96/23/96 |
| 3.77e+15 ohm-cm | 3.77e+15 ohm-cm | "A" | |
| Surface Resistance | 1.02e+15 ohm | 1.02e+15 ohm | C 96/23/96 |
| 1.57e+15 ohm | 1.57e+15 ohm | Cond. A | |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz | 3.2 @Frequency 1.00e+6 Hz | A |
| 3.54 @Frequency 60.0 Hz | 3.54 @Frequency 60.0 Hz | A | |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.167 - 0.201 W/m-K | 1.16 - 1.39 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 72.0 °C | 162 °F | Deflection Temp at unknown load |
| Processing Properties | Metric | English | Comments |
| Cure Time | 60.0 - 120 min @Temperature 150 - 160 °C | 1.00 - 2.00 hour @Temperature 302 - 320 °F | |
| 60.0 - 240 min @Temperature 160 - 180 °C | 1.00 - 4.00 hour @Temperature 320 - 356 °F | optional | |
| Pot Life | 220 min @Temperature 100 °C | 220 min @Temperature 212 °F | |
| Shelf Life | 5.00 - 8.00 Month | 5.00 - 8.00 Month | |