Abatron AboCast 8110-2/AboCure 8110-1 Flexible Epoxy物性表参数

吸水率 [%]: 4.5
弯曲强度 [MPa]: 16.3

Physical Properties	Metric	English	Comments

Water Absorption	4.5 % @Time 2.59e+6 sec	4.5 % @Time 720 hour	immersion; cured 30 days @ 25°C
	4.9 % @Time 2.59e+6 sec	4.9 % @Time 720 hour	immersion; cured 7 days @ 25°C
Viscosity	1600 cP	1600 cP

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	37 @Temperature 75.0 °C	37 @Temperature 167 °F	cured 7 days @ 25°C
	58 @Temperature 75.0 °C	58 @Temperature 167 °F	cured 30 days @ 25°C
	75 @Temperature 25.0 °C	75 @Temperature 77.0 °F	cured 7 days @ 25°C
	85 @Temperature 25.0 °C	85 @Temperature 77.0 °F	cured 30 days @ 25°C
	89 @Temperature -60.0 °C	89 @Temperature -76.0 °F	cured 30 days @ 25°C
	89 @Temperature -60.0 °C	89 @Temperature -76.0 °F	cured 7 days @ 25°C
Tensile Strength, Ultimate	16.3 MPa	2360 psi	cured 7 days @ 25°C
	37.9 MPa	5500 psi	cured 30 days @ 25°C
Elongation at Break	39 %	39 %	cured 30 days @ 25°C
	70 %	70 %	cured 7 days @ 25°C
Shear Strength	2.34 MPa @Temperature 75.0 °C	340 psi @Temperature 167 °F	Tensile, Al/Al lap joint; cured 7 days @ 25°C
	22.2 MPa @Temperature 25.0 °C	3220 psi @Temperature 77.0 °F	Tensile, Al/Al lap joint; cured 7 days @ 25°C
	30.8 MPa @Temperature 0.000 °C	4470 psi @Temperature 32.0 °F	Tensile, Al/Al lap joint; cured 7 days @ 25°C

Electrical Properties	Metric	English	Comments
Volume Resistivity	6.20e+7 ohm-cm @Temperature 100 °C	6.20e+7 ohm-cm @Temperature 212 °F	cured 30 days @ 25°C
	7.20e+8 ohm-cm @Temperature 100 °C	7.20e+8 ohm-cm @Temperature 212 °F	cured 7 days @ 25°C
	3.00e+12 ohm-cm @Temperature 25.0 °C	3.00e+12 ohm-cm @Temperature 77.0 °F	cured 7 days @ 25°C
	4.90e+13 ohm-cm @Temperature 25.0 °C	4.90e+13 ohm-cm @Temperature 77.0 °F	cured 30 days @ 25°C

Processing Properties	Metric	English	Comments
Pot Life	30 min @Temperature 25.0 °C	30 min @Temperature 77.0 °F	200 g

Descriptive Properties
Parts by Weight (pbw)	100		AboCast 8110-2
	9.7		AboCure 8110-1